Ceramic casting mold for casting metal and process for production thereof

ABSTRACT

Casting mold for metal casting, in particular precision casting of fine parts of steel, wherein at least the main part of the casting mold is comprised of porous ceramic with a high thermal coefficient of expansion which corresponds to the metal, and produced by generative rapid prototyping process, as well as generative rapid prototyping processes and coated powders particularly suitable therefore, as well as uses of the casting mold for tools and their components, in particular of steel.

BACKGROUND OF THE INVENTION

[0001] 1. Field of Invention

[0002] The invention concerns casting molds for casting metal, in particular the precision casting of fine parts and processes for production of casting molds which are based on a generative rapid prototyping process, as well as ceramic raw materials particularly suited for this process.

[0003] 2. Related Art of the Invention

[0004] In foundry technology the state of the art in the production of cast parts includes the use of lost wax sand or ceramic molds, which are not reused following casting.

[0005] The shaping of casting molds in the case of precision casting, ingot casting or shell casting is generally by a lost wax process or a related processes. Therein first a wax model of the final cast part is produced. The wax model is then coated a number of times with mold sand, which generally involves applying or coating an appropriate ceramic slip. The application of slip is carried out a number of times until the green mold exhibits sufficient shape stability in order to allow melting out of the wax, thereby forming a mold cavity in the casting mold. As a rule, the green casting mold must be fired prior to casting of metal, in order to pyrolyze organic additives (binders in particular) and to solidify the casting mold, turning it into ceramic. The term “turning into ceramic” is to be understood as referring to the firing or sintering of the green mold.

[0006] The lost wax process has the disadvantage that the wax model, in the following also referred to as the original model, must be produced by complex and intricate processes. Particularly in the case of producing prototypes various models must be individually constructed of wax. Due to the high thermal coefficient of expansion of wax great tolerance is allowed for dimensional trueness. Also considered disadvantageous therein is the additional process step of melting out the wax which, particularly in the case of relatively large models, translates into a supplemental expenditure in time.

[0007] One possibility for entirely dispensing with the manufacture of wax models and at the same time for providing an almost unlimited diversity of individual molds is provided by rapid prototyping processes (RP-process). Processes are known in which ceramic casting molds can be executed directly from computer models using generative RP-processes. Therein the casting molds are built up layer-by-layer with ceramic powder layers, which are built up and solidified, by adhesion or sintering, in selected areas into a three dimensional casting pre-mold. These processes are described in greater detail for example in U.S. Pat. No. 5,204,055. The disadvantage of this process includes that in general a substantially rougher surface is formed than in the case of the lost wax process. Typically, a step-like surface structure is formed, reflecting the thickness of the ceramic powder layers. Further, the complete removal of the residual not bound powder remaining in the inside of the mold leads to problems. This results in a lower surface quality, or to a penetration of the metal casting.

[0008] It is proposed in U.S. Pat. No. 6,109,332 to wash the surfaces of the cavities of the casting molds produced by generative RP-processes with solvent, or to flatten the step-like surfaces using a rubbing compound. This process however leads basically also to a removal or, in certain cases, a distortion of the desired precise structure.

[0009] A further series of problems is concerned with the dimensional trueness of the casting.

[0010] Metallic precision casting is carried out as a rule as a hot casting in which the casting mold is at temperatures of several 100° C. and, as a result of its thermal expansion, assumes a greater volume than in the cold state. After the casting of the metal the ceramic casting mold and the metal cool together from high temperatures to room temperature. As a rule the metal exhibits a substantially higher thermal coefficient of expansion than the ceramic, so that tensions and warping of the foundry casting can occur.

[0011] One approach to minimizing tensions and warping is described for example in EP 0 370 751 B1. It is proposed that the metal and ceramic are to be matched as closely as possible with respect to their thermal coefficient of expansion, in that a two-layer casting mold is built up. Therein the inner layer of the casting mold exhibits a higher thermal coefficient of expansion than the outer layer. The inner layer is preferably made of zircon (zirconium silicate) and aluminum oxide flakes. The casting mold is built up by coating wax models (lost wax process). This constructed geometric arrangement of the two layers is not producible by the known generative RP-process. Besides this, the zircon, at 4.5*10⁻⁶K⁻¹ , exhibits a relatively low thermal coefficient of expansion. The forestalling or retarding of the shrinkage of the cast metal, in particular mold cores, remains as before.

[0012] A further substantial influence on dimensional precision is inherent in the firing of the green casting mold. Firing leads to a reduction in volume of the casting mold. Only for the simplest of molds can this shrinkage be pre-calculated and compensated for by appropriate over-dimensioning of the original model.

SUMMARY OF THE INVENTION

[0013] It is thus the task of the present invention to provide a casting mold for metal casting, in particular precision casting, which provides a high surface quality and improves the dimensional trueness of the cast parts, as well as to provide a process and raw materials therefore, with which the casting molds can be produced in simple manner, in particular without the aid of original wax shapes.

[0014] The task is solved in that the casting mold for the metallic precision casting of fine parts is comprised at least substantial of a porous ceramic in the green or sintered state, of which the thermal coefficient of the expansion is greater than 7.5 μm/mK (7.5*10⁻⁶K⁻¹ ), wherein the casting mold is produced by a generative rapid,prototyping process, preferably employing powder mixtures of coated coarse particles and fine powder.

[0015] In accordance with the invention the casting mold is partially or entirely, at least however in substantial proportion, comprised of a porous ceramic with a high thermal coefficient of expansion. Thereby the difference between the thermal coefficient of expansion between the cast metal and casting mold is kept small and the thermal tensions following casting are substantially reduced. In particular, the incidences of warping or abnormal shrinkages brought about by the geometric shape of the casting mold is substantially reduced. The dimensional trueness of the casting is thereby substantially improved. The range of preferred thermal coefficient of expansion (TCE) of the ceramic depends upon the corresponding cast metal. For steel the TCE is preferably above 7.5*10⁻⁶K⁻¹ and particularly preferably in the range of 8.5 to 12*10⁻⁶K¹.

[0016] In particular in the field of precision casting structures, cutbacks and mold cores, having the TCE matched to the casting metal is of particular advantage. Thus, in the case that the casting mold is only in part made of the ceramic with high TCE, it is intended or provided that at least the precision mold structures and/or in certain cases the existing mold cores are produced of this ceramic. The term “mold cores” is in this context also intended to include all casting mold structures in which the casting metal is circumfluent over the major portion of their surface.

[0017] Suitable materials for casting molds include carbide, nitride and oxide ceramics, of which the TCE is above approximately 7.5*10⁻⁶K⁻¹. Particularly preferred are thus the oxide ceramics based on the elements Zr, Al, Mg. Particularly preferred are zircon partially stabilized with Ce, Mg or Y, Al/Zr-oxide, spinel and magnesium silicate.

[0018] Besides these main components, the oxide ceramic in accordance with the invention contains binder phases, which with respect to their sintering temperatures clearly differ from the main components of the casting mold. These binder phases are typically based on SiO₂ or silicates. The sintering temperature of the binder phases is preferably at least 50°C. below that of the remaining components. The temperature differential of the sintering temperatures is particularly preferably greater than approximately 100°C.

[0019] The strength or stability of the ceramic casting molds is thereby substantially determined by the proportion and the type of the binder phases, and establishes itself by the ceramic firing of the green mold or during heating of the green mold to the casting temperature.

[0020] In accordance with the invention the content of binder phases is reduced to the extent that no follow-up sintering of the ceramic casting molds during ceramic firing can occur, or as the case may be, no significant sintering shrinkage any longer occurs. It is particularly preferred that no significant sintering shrinkage occurs at temperatures below the casting temperature. The proportion of binder phases is thus limited to a few wt. % and typically lies below 7 wt. %.

[0021] The porosity of the ceramic casting molds is equivalent to the general range for ceramic casting molds as known from the state of the art.

[0022] The usual manner of proceeding for production of the ceramic casting molds does not involve ceramic firing.

[0023] A further inventive embodiment envisions, in contrast thereto, that the casting mold is constructed at least in part of green ceramic (green mold). For example, the main proportion of the casting mold can be ceramic and a core or incorporated parts or inlays or inserts can be present in the green state. The green parts of the mold thus still contain, at least prior to heating of the casting mold to casting temperatures, some organic binders. The proportion of organic binders is generally in the range of 1 to 10 wt. %. Therein carbonizing organic binders, that is, binders which during pyrolysis form a high carbon residue, are preferred. The organic binders are partially or completely pyrolyzed during heating depending upon the temperature and time of heating. A high proportion of organic binders could in preferred manner increase the porosity of the casting mold.

[0024] The dispensing with the separate step of ceramic firing of the green casting molds provides a further important process advantage.

[0025] The inventive casting molds are in particular suited for the precision casting of metal alloys or refractory alloys with an average thermal coefficient of expansion in the range of 5 to 14*10⁻⁶K⁻¹ (average value over temperature interval 0 to 800° C.).

[0026] Among the metal alloys which cooperate particularly well with the inventive casting molds are steels, ferritic, martensitic steels, Fe/Ni—, Fe/Ni/Co— or Ni-alloys.

[0027] Included in the particularly preferred steels are, in particular, the acid resistant steels with steel code numbers 1.4059, 1.4085, 1.4086, 1.4136, 1.4138 with a thermal coefficient of expansion of approximately 11.5*10⁻⁶K⁻¹, and the particularly heat resistant steels 1.4710, 1.4729, 1.4740, 1.4743 with a thermal coefficient of expansion of approximately 13.5*10⁻⁶K⁻¹. (The numbers are with reference to the “Steel Codes”, publishing house Steel Codes GmbH, Marbach, 2001 Edition).

[0028] The cast parts can be employed for example as parts of mold or shaping tools or as prototypes and for small run production in automobile construction.

[0029] In accordance with the invention it is provided or intended that the casting molds, or at least their essential parts, are produced by generative rapid prototyping process (RP).

[0030] The term generative RP is intended to include processes which include at least the following essential shaping steps:

[0031] a) applying a layer of particles (powder layer) onto a substrate;

[0032] b) flattening the applied layer with a flattening device;

[0033] c) hardening the applied layer in defined areas

[0034] by adhering the particles under the influence of binder liquid,

[0035] or by melting or sintering the particles under the influence of intensive electromagnetic radiation, in particular laser radiation,

[0036] or adhering the applied layer by light induced hardening of organic binders.

[0037] By repeating steps a) through c) a number of times the green shape is built up by successive layers.

[0038] In accordance with the invention it is provided that the powder particles are comprised of ceramic material with an average thermal coefficient of expansion above 7.5*10⁻⁶K⁻¹.

[0039] A further aspect of the invention is concerned with ceramic powder mixtures particularly suited for the process.

[0040] In one advantageous embodiment of the invention powder mixtures of coarse material and fine material are employed, wherein the fine material has a significantly higher sinterability than the coarse material. The sintering temperature of the fine particles lies in accordance with the invention at least 50° C. below that of the coarse particles. By this combination of sinterable fine material and less sinterable coarse material a limiting of the sintering shrinking is achieved during ceramic firing of the green casting mold. The sintering is essentially confined to the fine particles which form the binder phase.

[0041] The inventive powder composition is an important contributor to the dimensional stability or trueness of the casting.

[0042] The fine material is also referred to herein as ceramic binder, which in the ceramic form is the binder phase. The coarse material is particularly comprised of the already discussed oxide ceramics based on Al, Zr and/or Mg, while the fine material or the ceramic binder is based on SiO₂ and/or silicates.

[0043] In accordance with the invention there is a clear particle size difference between coarse and fine material. With regard to the particle size distribution there is thus a clear particle size gap. Typically the average particle size of the coarse particle is above 10 μm and the average particle size of the fine particles is below 5 μm. Therein the average particle size of the large material should be at least the 10 fold of the average particle size of the fine material. It is particularly preferred when the fine particle is nano-powder, for example pyrogenic SiO₂ or aluminum oxide.

[0044] The coarse material could just as well be agglomerations of smaller particles. Therein agglomerates of particles with an average diameter range of approximately 1 to 5 μm are found particularly preferable.

[0045] A further embodiment of the invention envisions that the powder employed for generative RP-process is comprised primarily of coated particles. Therein at least the coarse particles are provided with a coating. The fine particles may be present as the second, generally uncoated, powder component. Preferably the fine particles are however bound in or onto the coating. If nano-particles are employed ,these are typically a component of the coating of the coarse particles.

[0046] A further aspect of the invention is concerned with the preferred shaping process involving generative RP.

[0047] In a preferred process embodiment of generative RP, a 3D-binder printing process is employed. The solidification of the particle layers is therein brought about by the influence of binder liquid, which is applied to the layer by means of a liquid dispensing printer head. The adhesive effect can be caused by components of the binder liquid or by components in the powder, of which the adhesive effect is activated by the influence of the liquid.

[0048] Preferably employed herein is the combination of coated powders, of which the coating includes polymers which are readily soluble in organic solvents and binder liquids comprising organic solvents. The polymers suitable for the invention include in particular poly(meth)acrylate, polyvinyl alcohol, polyvinyl acetate, polyvinyl pyrolidone, or polyvinyl butyral, exclusively or as mixtures. The binder liquids suitable for the invention include in particular mixtures which contain the C2- through C7-alcohols, for example ethyl alcohol, (iso)propanol or n-butanol, C3- through C8-ketones such as for example acetone or ethyl-methyl-ketone, cyclic ethers such as tetrahydrofuran, or polyethers such as dimethoxyethanol or dimethoxydiethylene glycol. In the case of the use of wax-type coatings, low molecular aliphatic carbohydrates, in particular cyclic or linear C6- through C8-aliphatics, are preferred.

[0049] In a further preferred process embodiment, laser sintering is employed. The solidification of the particle layers is herein caused by melting or sintering of the particles to each other. The melting and sintering can be limited to only certain components of the powder mixture. This is, for example, the case when the powder mixture is comprised of ceramic and polymer particles, wherein then only the polymer particles are melted or sintered.

[0050] In yet a further variation of the inventive process, polymer coated ceramic powder particles are employed. Therein the laser output is so adjusted that essentially only a melting and/or sintering of the polymer component occurs; a ceramic sintering process is however precluded. As polymers there are employed thermoplastics, for example poly(meth)acrylate or a duroplastic such as, for example, phenol resin. In the case of the duroplastic under the influence of the laser radiation a carbonization of the material is caused, whereby a solidified carbonatious residue is formed. The polymers are particularly preferably a component of coated ceramic particles.

[0051] The already discussed powder mixtures of coarse and fine components can also be employed in the laser sintering process in analogous manner.

[0052] A further aspect of the invention is concerned with the construction of the casting mold.

BRIEF DESCRIPTION OF THE DRAWINGS

[0053] Advantageous embodiments of the invention are described in greater detail in the following on the basis of the figures. The figures are only exemplary and serve for explanation of the invention. In the invention is not limited to the described embodiments of the invention.

[0054] Therein there is shown:

[0055]FIG. 1 Cross-section of a casting mold produced by a generative RP-process comprised of porous ceramic (1), mold cavity (2) and geometric receiving volume area (3)

[0056]FIG. 2 Cross-section of a casting mold produced by means of a generative RP-process, comprised of porous ceramic (1), with mold cavity (2), geometric receiving volume area (3), mold core (4) and ribs (5)

[0057]FIG. 3 Cross-section of an assembled casting mold with mold cavity (2), with a shell (6) of mold sand and an insert (7) produced by a generative RP-process, exhibiting a geometric receiving volume area (3)

[0058]FIG. 4 Cross-section of a casting mold of porous ceramic (1) with supporting ribs (8) and a back fill (9) of loose ceramic

DETAILED DESCRIPTION OF THE INVENTION

[0059] Although the generative RP-processes are particularly suitable for the integral production of even complex casting mold geometries, it is not outside the scope of the invention that the casting mold contain additional parts, for example, support or reinforcing or coating or casing parts (in the following also referred to as mold shell), which are produced by another process.

[0060] In accordance with the invention the mold insert (7), in particular the mold part with the highest geometric requirements, is produced by generative RP-processes (see FIG. 3). The shell (6) or, as the case may be, the reinforcing or casing part of the assembled casting mold, is preferably formed by more economical mold sand, for example quartz sand or zircon sand. The reduced dimensional trueness and casting surface quality in the area of the reinforcing and casing structures can generally be accepted without problem, since the highest quality requirements in the cast parts are as a rule limited to only selected geometrically sophisticated or exacting areas (3), while over large areas in part greatly reduced requirements exist or resort may be had to a very simple follow-up processing.

[0061] This can be of advantage in particular in the case of comparatively smaller geometric exacting areas (3). Also for simple mold core geometries, or if a different material is to be employed for the mold core, this aggregated process is useful.

[0062] In a further variant neither casting molds nor cores nor inserts are fired, but rather submitted to the casting process while in the green state. The green part is formed in particular by polymer-bound ceramic powder based on ZrO₂ and/or Al₂O₃, in certain cases with ceramic binders.

[0063]FIG. 2 shows the inventive variant of an assembled casting mold, wherein the casting mold (1) is comprised of green or fired ceramic as the mold shell and a mold core (4) extending through the mold cavity (2) in the form of green or fired ceramic. The mold core (4) defines for example cooling channels or securing channels of the cast object.

[0064] Preferably, the structures corresponding to the mold core (according to (4), FIG. 2) in certain cases the structures which are flowed-about to a great extent by the casting metal, are likewise produced by generative RP. It is particularly preferred when the entire casting mold is formed integrally in a single generative RP-process.

[0065] By the generative RP-process it is likewise possible in simple manner to precisely produce the exterior shape of the casting mold. For example it is possible to provide cooling channels on or in the outside of the casting mold, or flow gates or risers. FIG. 2 shows an example of an embodiment with exterior ribs (5) which have the effect of cooling channels.

[0066] In FIG. 4 a further embodiment of the invention is shown. This shows a cross-section through a casting mold of porous ceramic (1), which carries supporting ribs (8) on the side opposite to the mold cavity (2). The casting mold is back-fed with loose ceramic (9) for the casting or pouring of the metal. The fill provides the comparatively thin casting mold produced by generative 3D-PR-process with the mechanical stability necessary for casting. The fill is comprised preferably of mold sand or refractory sand based on SiO₂, silicates or zirconium.

[0067] In the simplest case the entire casting mold is formed integrally by means of generative RP and exhibits no mold core.

[0068] A preferred use of the inventive casting molds is in the production of tools, in particular in the manufacture of die casting tools. 

1-20. (Cancelled)
 21. A casting mold for metallic foundry or for precision casting of fine parts, wherein the casting mold, or at least a part thereof, is produced by a generative rapid prototyping process, and is mainly comprised of a porous ceramic in the green or sintered state, wherein the thermal coefficient of expansion of the ceramic is above approximately 7.5*10⁻⁶K⁻¹ and the ceramic is comprised of coated ceramic coarse particles and sinterable ceramic fine particles wherein the sintering temperature of the fine particles is at least 50° C. below that of the coarse particles.
 22. A casting mold according to claim 21, wherein the main part of the casting mold includes at least one insert and/or a mold core.
 23. A casting mold according to claim 21, wherein the casting mold includes reinforcing ribs produced using a generative rapid prototyping process.
 24. A casting mold according to claim 21, wherein, at least during casting, the casting mold is back-fed with a fill of ceramic material.
 25. A casting mold according to claim 21, wherein the generative prototyping process is 3D-binder printing or 3D-laser sintering.
 26. A casting mold according to claim 21, wherein the porous ceramic includes as main component aluminum oxide, zirconium oxide, magnesium silicate, spinel and/or magnesium oxide.
 27. A casting mold according to claim 21, wherein the porous ceramic includes 0.5 to 10 wt. % organic binder.
 28. A method for precision casting of metal alloys, comprising selecting a metal or metal alloy to be cast, determining the average thermal coefficient of expansion of said metal or alloy at foundry temperatures, forming a green casting mold, said mold adapted for metallic foundry or for precision casting of fine parts, by a generative rapid prototyping process, wherein said mold is mainly comprised of a porous ceramic in the green or sintered state, wherein the thermal coefficient of expansion of the ceramic is above approximately 7.5*10⁻⁶K⁻¹ and wherein the ceramic is comprised of coated ceramic coarse particles and sinterable ceramic fine particles, wherein the sintering temperature of the fine particles is at least 50° C. below that of the coarse particles, optionally sintering said mold, casting metal into said green or sintered mold to form metal parts, wherein the mold material is selected such that the average thermal coefficient of expansion of the mold material in contact with said metal is approximately that of the metal or alloy being cast, and over the temperature interval of 0 to 800° C., is in the range of 5 to 14*10⁻⁶K⁻¹.
 29. A method for casting molds according to claim 28, wherein said metal or alloy is cast by ingot casting, shell casting or precision casting, and wherein said metal or alloy is selected from the group consisting of steel and Fe/Ni—or Fe/Ni/Co— or Ni-alloys.
 30. A process for producing a green casting mold for metallic foundry or for precision casting of fine parts, wherein the casting mold is produced by a generative rapid prototyping process and is mainly comprised of a porous ceramic in the green or sintered state, wherein the thermal coefficient of expansion of the ceramic is above approximately 7.5*10⁻⁶K⁻¹ and that the ceramic is comprised of coated ceramic coarse particles and sinterable ceramic fine particles, wherein the sintering temperature of the fine particles is at least 50° C. below that of the coarse particles, and wherein said process comprises repeating sequence of the steps: a) applying a layer of particles, using a dispensing device, onto a substrate; b) flattening the applied layer with a flatten device; c) hardening the layer in defined areas by adhering the particles under the influence of binder liquid, or by melting or sintering the particles under the influence of intensive radiation, wherein the majority of the particles have an average thermal coefficient of expansion of above approximately 7.5*10⁻⁶K⁻¹, wherein the ceramic is comprised of coated ceramic coarse particles and sinterable ceramic fine particles, and wherein the sintering temperature of the fine particles is at least 50° C. below that of the coarse particles.
 31. A process according to claim 30, wherein at least the coarse particles are coated with organic polymers.
 32. A process according to claim 30, wherein the green casting mold is converted into a porous casting mold by ceramic firing.
 33. A process according to claim 30, wherein in the green or ceramic casting mold at least one mold core and/or insert of green and/or fired ceramic is employed based on MgO, ZrO₂, spinel, and/or Al₂O₃.
 34. A process according to claim 30, wherein the green casting mold is a mold core or insert, which while in the green or fired state is inserted or introduced into a support or casing mold, whereby an composite casting mold is formed.
 35. A process according to claim 30, wherein the support or reinforcing or casing mold includes foundry sand based on SiO₂, silicates or zircon.
 36. A powder mixture for producing inserts for cast molds for metallic foundry or for precision casting of fine parts, wherein said powder mixture includes coated ceramic coarse particles and sinterable ceramic fine particles, wherein the sintering temperature of said fine particles is at least 50° C. below that of the coarse particles.
 37. A powder mixture according to claim 36, wherein the coating is comprised essentially of polymers which are readily soluble in organic solvent.
 38. A powder mixture according to claim 36, wherein the ceramic coarse particles include oxides of the elements Mg, Al and/or Zr, and the ceramic fine particles are comprised essentially of SiO₂, and/or silicates.
 39. A process according to claim 30, wherein said casting is a tool or tool component for die casting, injection molding or forging machines.
 40. A process according to claim 30, wherein said casting is a tool or tool component having cooling channels. 